cold work tool steel 1.2360 / DIN X48CrMoV8-1-1 round bar/Flat bar

1.cold work tool steel 1.2360 / DIN X48CrMoV8-1-1 round bar 2.Certificate: ISO 9001:2008 3.Quality assurance 4.Manufacturer

1. cold work tool steel 1.2360 / DIN X48CrMoV8-1-1 round bar /Flat bar

 

2.Chemical Composition:

Element	C	Si	Mn	Cr	Mo	V	P	S
content	0.5	1.05	0.45	8.00	1.50	0.52	≤0.003	≤0.005

 

3.the performance advantages and the uses

 

Severely stressed machine blades for cellulose and paper ind., woodworking milling cutters, flat and circular blades for cutting 5 to 15 mm thick sheet/plate.  

4.Soft AnnealingHeat to 820-860oC, cool slowly in furnace. This will produce a maximum Brinell hardness of 250.5.Stress RelievingStress relieving to remove machining stresses should be carried out by heating to 650oC, holding for one hour at heat, followed by air cooling. This operation is performed to reduce distortion during heat treatment.6.HardeningHarden from a temperature of 1000-1040oC followed by oil or air quenching. Hardness after quenching is 57 HRC.

7.Our smelting facilities data as following:

45 tons EBT, 50 tons EF, 50 tons VOD

Forging equipment :a 3200 tons pressing machine , a 2000 tons pressing machine, a 1000 tons pressing machine, a 8 tons Hydraulic hammer, a 3 tons Hydraulic hammer

Processing equipment:  8 of gantry millings, 12 of lathe machines etc.

8.Tech: EAF+LF+VD /+ESR

Melting process:electric arc furnace, ladle furnace,vacuum degassing

 

Remelting process: Electroslag remelting

 

Casting process: ingot casting

 9.Test and inspection: 100% mixed test

 

100% crack test,defect depth max.1% of diameter(turned, peeled) or width

 

100% US test acc. to SEP standard.